Shear bond strength of an autopolymerizing repair resin to injection-molded thermoplastic denture base resins

Abstract

Objective. This study investigated the shear bond strength of an autopolymerizing repair resin to injection-molded thermoplastic denture base resins. Materials and methods. Four injection-molded thermoplastic resins (two polyamides, a polyethylene terephthalate copolymer and a polycarbonate) were used in this study. The specimens were divided into eight groups according to the type of surface treatment given: (1) no treatment, (2) air abrasion with alumina, (3) dichloromethane, (4) ethyl acetate, (5) 4-META/MMA-TBB resin, (6) alumina and 4-META/MMA-TBB resin, (7) tribochemical silica coating or (8) tribochemical silica coating and 4-META/MMA-TBB resin. Half of the specimens in groups 1, 5, 6 and 8 were thermocycled for 10,000 cycles in water between 5–55°C with a dwell time of 1 min at each temperature. The shear bond strengths were determined. Results. The shear bond strengths to the two polyamides treated with alumina, dichloromethane and ethyl acetate and no treatment were very low. The greatest post-thermocycling bond strengths to polyamides were recorded for the specimens treated with tribochemical silica coating and 4-META/MMA-TBB resin (PA12: 16.4 MPa, PACM12: 17.5 MPa). The greatest post-thermocycling bond strengths to polyethylene terephthalate copolymer and polycarbonate were recorded for the treatment with alumina and 4-META/MMA-TBB resin (22.7 MPa, 20.8 MPa). Conclusion. Polyamide was exceedingly difficult to bond to an autopolymerizing repair resin; the shear bond strength improved using tribochemical silica coating followed by the application of 4-META/MMA-TBB resin. Both polyethylene terephthalate copolymer and polycarbonate were originally easy to bond to an autopolymerizing repair resin. However, with 4-META/MMA-TBB resin, the bond was more secure.

Key Words::

• injection-molded thermoplastic denture base resin
• polyamide
• polyethylene terephthalate copolymer
• polycarbonate
• shear bond strength

Declaration of interest: The authors report no conflicts of interest. The authors alone are responsible for the content and writing of the paper.