Semi-IPN chitosan/polyvinylpyrrolidone microspheres and films: sustained release and property optimisation

, , , &
Pages 762-770 | Received 26 Aug 2012, Accepted 25 Feb 2013, Published online: 02 May 2013
 

Abstract

A set of chitosan-polyvinylpyrrolidone (CH-PVP) microspheres were prepared as semi-inter penetrating networks (semi-IPN) and loaded with 5-fluorouracil. In vitro release studies showed faster release for semi-IPN microspheres compared to pure CH samples, and the total release was achieved in about 20–30 days, depending on the composition. In vitro cell studies were achieved against human breast adenocarcinoma cell line cells where adsorption of cells on microspheres with a significant decrease in their number was obtained. Meanwhile, the CH-PVP films, which were prepared with the same compositions as in the microspheres, demonstrated an increase in strength from 66 to 118 MPa as the PVP content was decreased. It can be concluded that the prepared CH-PVP semi-IPN microspheres are novel promising carriers compared to pure CH microspheres since it becomes possible to adjust stability and hydrophilicity of the microspheres as well as the release rates of the drugs from the microspheres by changing the ratio of CH/PVP composition.

Acknowledgements

Authors are thankful to the METU-BAP Grants supporting the study.

Reprints and Corporate Permissions

Please note: Selecting permissions does not provide access to the full text of the article, please see our help page How do I view content?

To request a reprint or corporate permissions for this article, please click on the relevant link below:

Academic Permissions

Please note: Selecting permissions does not provide access to the full text of the article, please see our help page How do I view content?

Obtain permissions instantly via Rightslink by clicking on the button below:

If you are unable to obtain permissions via Rightslink, please complete and submit this Permissions form. For more information, please visit our Permissions help page.