Abstract
The aim of the study was firstly to investigate the influence of moisture on the tableting and tablet properties of Kollidon SR and secondly to investigate the influence of theophylline monohydrate on the tableting behavior and tablet properties produced from binary mixtures with Kollidon SR. In comparison to Kollidon SR, microcrystalline cellulose (MCC) was used. The glass transition temperature (Tg) of the powder over the whole range of RH (0–90%), and in addition, the Tg of tablets of Kollidon SR were measured. Densities and flowability of the powders were analyzed. The tablets were produced at five different maximum relative densities (ρrel, max) on an instrumented eccentric tableting machine. They were produced at three different relative humidities (RH), 30%, 45%, and 60% RH for the pure substances and binary mixtures with different ratios of drug and excipient were tableted at 45% RH. The tableting properties were analyzed by 3D modeling, force-displacement profiles, and compactibility plots. First, the Tg of the powder decreased with increasing RH and the Tg of the tablet was 4–8 K lower than the powder. The predominant deformation of Kollidon SR is plastic deformation and Kollidon SR showed a higher compactibility than MCC. The parameters of the 3D model showed an extreme change between 45 and 60% RH, and at higher RH more and more particles deformed elastically. This was confirmed by analysis of force-displacement profiles. At 60% RH, the radial tensile strength of the Kollidon SR tablets was half of the radial tensile strength at 45% RH. The reason is a higher relative energy of plastic deformation than for MCC. This results in a better utilization of the energy to deform the powder into a tablet and the exceeding of the glass transition temperature at higher RH. In conclusion, at 60% RH at the same ρrel, max, tableting and tablet properties of Kollidon SR are extremely changed since plasticity is significantly higher. In the second part of the study, the insufficient flowability of theophylline monohydrate can be compensated by using Kollidon SR in a mixture with up to 20% theophylline. Further, pressure plasticity ε of MCC and Kollidon SR was lowered in the mixture with theophylline monohydrate. The same is valid for the compactibility. The influence of theophylline monohydrate on the pressure plasticity e of the mixtures was better compensated in the mixture with MCC than in a mixture with Kollidon SR. This compensation was also visible by analyzing the force-displacement-profiles. However, hardly any influence on the radial tensile strength could be detected. Kollidon SR and Kollidon SR mixtures exhibited a higher compactibility than MCC and MCC mixtures. The differences became smaller with increasing theophylline content.