Preparation and characterization of an iron oxide-hydroxyapatite nanocomposite for potential bone cancer therapy

Abstract

Recently, multifunctional magnetic nanostructures have been found to have potential applications in biomedical and tissue engineering. Iron oxide nanoparticles are biocompatible and have distinctive magnetic properties that allow their use in vivo for drug delivery and hyperthermia, and as T₂ contrast agents for magnetic resonance imaging. Hydroxyapatite is used frequently due to its well-known biocompatibility, bioactivity, and lack of toxicity, so a combination of iron oxide and hydroxyapatite materials could be useful because hydroxyapatite has better bone-bonding ability. In this study, we prepared nanocomposites of iron oxide and hydroxyapatite and analyzed their physicochemical properties. The results suggest that these composites have superparamagnetic as well as biocompatible properties. This type of material architecture would be well suited for bone cancer therapy and other biomedical applications.

Video abstract

Point your SmartPhone at the code above. If you have a QR code reader the video abstract will appear. Or use:

http://youtu.be/rRFw0_DBkBU

Keywords:

• iron oxide
• hydroxyapatite
• nanocomposite
• superparamagnetic
• bone cancer

Introduction

Cancer is the most dreaded disease, along with heart disease. Hyperthermia has attracted much interest in the treatment of cancer due to its advantages over chemotherapy and radiotherapy. Using hyperthermia, cancer cells are killed directly within a short period of time, whereas normal cells are unaffected.¹ Magnetic hyperthermia is practiced by applying an external alternating magnetic field which in turn oscillates the magnetic moment of each particle, converting magnetic energy into heat. Superparamagnetic materials for magnetic hyperthermia are promising candidates for antitumor therapy because they have the capacity to destroy deep tumors and are controlled by an external magnetic field.² Magnetic nanoparticles have attractive features that could be used effectively in nanomedicine. First, they have a controllable particle size (from a few nanometers to tens of nanometers). Second, they are magnetic, so can be manipulated by an external magnetic field. Third, they can be made to heat up, so can be used as hyperthermia agents, delivering large amounts of thermal energy to tumor cells and destroying them.³ If an iron oxide nanoparticle is below 45 nm in size, it is classified as superparamagnetic due to its line-type hysteresis loop iron oxide nanoparticles. The magnetite (Fe₃O₄) phase of superparamagnetic iron oxide nanoparticles has numerous in vivo applications, since it can respond to an external stimulus and heat up, and does not retain any magnetism after removal of the external magnetic field.^4,5 Materials that are compatible with bone tissue are preferred for bone repair and hard tissue engineering.⁶ Hydroxyapatite (HAp) is widely used in this setting because of its exceptional biocompatibility, bioactivity, and osteoconductivity.⁷ A number of researchers have developed a variety of HAp-based magnetic materials for hyperthermia-based treatment of cancer.^8–11

Murakami et al prepared a porous Fe₃O₄-HAp composite using a hydrothermal method. The composite holds 30% Fe₃O₄ in cages of rod-shaped HAp particles.⁸ Fe₃O₄ nanoparticles are prepared by a coprecipitation method, and a horizontal tumbling ball mill is used to mechanochemically synthesize submicron-sized HAp particles. According to Iwasaki et al⁹ this process promotes the dispersion of Fe₃O₄ nanoparticles in the HAp matrix. The magnetic Fe₃O₄ particles are coated with HAp by spray-drying. Donadel et al found that the spray-drying technique is an efficient and inexpensive method for creating spherical particles with a core/shell structure.¹⁰ Tampieri et al prepared iron-doped HAp endowed with superparamagnetic properties for hyperthermic application.¹¹

These composites can be synthesized conventionally by mixing HAp nanopowder with Fe₃O₄ nanoparticles that are prepared separately. In this work, Fe₃O₄ nanoparticles were prepared by alkaline coprecipitation of ferric and ferrous chloride in aqueous solution. Nanocrystalline HAp was prepared using an optimized sol-gel method. Dry (zirconia ball) milling was used to blend the Fe₃O₄-HAp (0.70 w/w) nanoparticles. The Fe₃O₄-HAp nanoparticles and their composite were analyzed by Fourier transform infrared spectroscopy, diffuse reflectance spectroscopy, scanning electron microscopy, thermogravimetric analysis, differential scanning calorimetry, vibrating sample magnetometry, and cytotoxicity tests. The method proposed in this paper is easy and cost-effective for preparing these nanocomposites. The synthesis and characterization of this biocompatible magnetic biomaterial is explained in detail, and the nanostructured Fe₃O₄-HAp composite is ideal for bone cancer therapy.

Materials and methods

Synthesis of iron oxide nanoparticles

Fe₃O₄ magnetic nanoparticles were synthesized by the alkaline coprecipitation method. The molar ratio of Fe³⁺:Fe²⁺ chloride was maintained at 2:1. The prepared magnetite was black in color and the pH was maintained between 9 and 14.¹² The overall reaction is written as:

${\text{Fe}}^{2+}+2{\text{Fe}}^{3+}+8{\text{OH}}^{-}\to {\text{Fe}}_3{\mathrm{O}}_4+4{\mathrm{H}}_2\mathrm{O}$(1)

Synthesis of HAp nanoparticles

The HAp nanoparticles were prepared by the wet chemical route method. First, 0.25 M phosphoric acid was prepared in distilled water. Ammonia (NH₃) was added to this solution, with stirring to maintain the pH at 10. Next, a 1 M calcium nitrate tetrahydrate solution was prepared by dissolving in double-distilled water, which was then added slowly to the above phosphoric acid-ammonia solution. The solution was stirred vigorously for 1 hour and allowed to age at room temperature for 24 hours. The gel obtained after aging was dried at 80°C for 48 hours in a dry oven. The resulting mixture were washed repeatedly using distilled water. After washing, the powder was sintered for 2 hours at a temperature of 900°C.

Synthesis of Fe₃O₄-HAp nanocomposites

The Fe₃O₄-HAp nanocomposites were prepared using a wet-type ball mill (Figure 1A). The ratio of HAp to Fe₃O₄ nanoparticles was 1.5:1 (w/w). Ball milling was carried out for 5 hours using a zirconia bowl and ball at 300 rpm, with a ball to sample powder ratio of 10:1 (w/w).

Figure 1 (A) Fe₃O₄-HAp nanoparticles in powder form. (B) Fourier transform infrared spectra of HAp, Fe₃O₄, and Fe₃O₄-HAp nanoparticles. (C) Diffuse reflectance spectra of magnetite and the composite. (D) Scanning electron micrograph of Fe₃O₄-HAp nanoparticles.

Abbreviations: Fe₃O₄, iron oxide; HAp, hydroxyapatite.

Characterization

Fourier transform infrared spectra were taken using an 8400S spectrophotometer (Shimadzu, Tokyo, Japan). KBr pellets were used, and the spectra were recorded in aqueous medium.

The morphology of the Fe₃O₄-HAp nanostructures was observed using a scanning electron microscope (ICON, Quanta 200 Mark II Environmental scanning electron microscope) with an acceleration voltage of 0.2–30 kV.

The thermal properties of the prepared nanocomposites were investigated using a thermal analyzer (STA 449 F3 Jupiter, Netzsch Gerätebau GmbH, Selb, Germany) along with thermogravimetry and differential scanning calorimetry in the temperature range of 28°C–1,100°C at a heating rate of 20°C per minute in a dry air atmosphere. Al₂O₃ was used as the reference material.

Diffuse reflectance spectroscopy was performed using a Specord 210 Plus (Analytik Jena, The Woodlands, TX, USA) between 190 and 1,100 nm at room temperature.

The superparamagnetic properties of the Fe₃O₄-HAp nanocomposites were studied using a 7410 vibrating sample magnetometer (Lake Shore, Westerville, OH, USA), in atmospheric air at room temperature.

The cytotoxic effects of the Fe₃O₄-HAp nanocomposites were evaluated using MG63 cells. The MTT assay was performed according to the procedure shown in Figure 2. The formazan was dissolved in dimethyl sulfoxide and the absorbance of the solution was quantified at 510 nm.

Figure 2 Flow chart showing the MTT assay procedure.

Results and discussion

Fourier transform infrared spectroscopy

The Fourier transform infrared spectral assignments for pure Fe₃O₄, HAp, and the Fe₃O₄-HAp nanoparticles are shown in Figure 1B and tabulated in Table 1. From these data, the functional groups of prepared samples confirms the presence of pure Fe₃O₄ and pure HAp. IN Fe₃O₄-HAp nanoparticles, a slight variation in spectral assignments confirms the close interaction between Fe₃O₄ and HAp.

Table 1 Fourier transform infrared spectral assignments of pure Fe₃O₄, HAp, and Fe₃O₄-HAp nanoparticles

S No	Wave number (cm^−1)			Spectral assignments
	Fe3O4	HAp	Fe3O4-HAp
1	–	3,639	3,639	OH^− group, CaO
2	–	3,561	3,570	Stretching mode of OH^− group
3	3,420	–	3,420	H2O, OH^− group
4	–	2,080	–	Phosphate group (PO4^3−)/absorbed CO3^2−
5	–	2,003	–	Phosphate group (PO4^3−)/absorbed CO3^2−
6	–	–	1,638	O-H in-plane bending
7	1,625	–	–	(H-O-H) adsorbed water
8	–	1,473	1,473	CO3^2−
9	1,383	–	–	N-O nitro compounds
10	1,151	–	–	C-O
11	–	–	1,091	Phosphate group (PO4^3−)
12	1,062	–	–	C-O
13	–	1,046	1,046	Phosphate group (PO4^3−)
14	–	–	960	Phosphate group (PO4^3−)
15	891	–	–	C-H
16	–	–	875	C-H
17	797	–	–	C-H
18	–	–	629	C-Cl
19	–	–	601	O-P-O bending
20	588	–	–	Fe-O-Fe bond (Fe ions in tetrahedral and octahedral site)
21	–	566	566	O-P-O bending

Abbreviations: Fe₃O₄, iron oxide; HAp, hydroxyapatite.

Diffuse reflectance spectroscopy

Diffuse reflectance spectroscopy provides the electron transition of pure and mixed samples. Figure 1C represents the diffuse reflectance spectra for pure Fe₃O₄ and Fe₃O₄-HAp. Pure Fe₃O₄ shows a wavelength (⁴T_l) transition in the range of 780–830 nm and an electron pair transition of 510 nm. This shows a higher position of the ligand-to-metal charge transfer transition and pair transition band of red Fe₃O₄.

Scanning electron microscopy

The micromorphology and texture of the Fe₃O₄-HAp nanocomposites are shown in Figure 1D. This scanning electron microscopic image shows that pure Fe₃O₄ has an irregular approximately spherical-like morphology with an average particle size in the range of 50–70 nm and that HAp has a particle size in the range of 30 – 40 nm. The aggregated Fe₃O₄-HAp clusters have a size range of 100–350 nm and both phases distributed uniformly, as shown in Figure 1D. The characteristic dark and light gray represents the Fe₃O₄ and HAp, respectively.

Thermogravimetric analysis

The Fe₃O₄-HAp nanoparticles were studied by thermogravimetric analysis in a nitrogen atmosphere at a heating rate of 20°C per minute. Figure 3 shows the thermogravimetric analysis curves, depicting the variations in residual mass of the samples with increasing temperature. The absolute weight loss from the uncoated Fe₃O₄ is nearly 17% for the whole temperature range due to removal of adsorbed physical and chemical water. Another 5% weight loss was seen from 160°C to 300°C, and this was associated with decomposition of residual chemical compounds. No significant weight loss was observed at higher temperatures. Thermogravimetric analysis of the Fe₃O₄-HAp powder showed weight loss up to a temperature of 800°C and thereafter weight remained constant.

Figure 3 Weight loss from the Fe₃O₄-HAp nanoparticles.

Abbreviations: Fe₃O₄, iron oxide; HAp, hydroxyapatite; NPs, nanoparticles.

The first stage of weight loss is between 90°C and 390°C, which corresponds to dehydration of the precipitating complex and loss of physically adsorbed water molecules from the HAp powder. The weight loss in this region is 10%. Stage 1 corresponds to vaporization of adsorbed water on the surface of HAp, stage 2 is due to vaporization of the water and crystallization of HAp, and stage 3 is probably due to breakage of CO₃²⁻ and HPO₄ in HAp.

Differential scanning calorimetry

The differential scanning calorimetry analysis of Fe₃O₄ and the nanocomposite is shown in Figure 4. The pure Fe₃O₄ shows a strong endothermic peak approximately 100°C. This is due to removal of the solvent molecule (H₂O). A slight endothermic transition approximately 620°C indicates crystallization of the magnetite phase. The differential scanning calorimetry results for the Fe₃O₄-HAp nanocomposite show a strong endothermic peak located in the range of 90°C–110°C. Two exothermic peaks were identified at 470°C and 720°C. The first one could be due to crystallization of the powder, given that this temperature range allows strong interaction between Fe₃O₄ and HAp molecules. The second one corresponds to the rearrangement of the CO₃²⁻ and HPO₄⁻ groups present in HAp. This is in good agreement with the thermogravimetric analysis.

Figure 4 DSC analysis of Fe₃O₄-HAp nanoparticles.

Abbreviations: DSC, differential scanning calorimetry; Fe₃O₄, iron oxide; HAp, hydroxyapatite; NPs, nanoparticles.

Vibrating sample magnetometry

The magnetic hysteresis loops for the Fe₃O₄ nanoparticles and the Fe₃O₄-HAp nanocomposites is shown in Figure 5. These materials exhibited strong magnetic behavior, with saturation magnetization of 20.639 and 7.34 emu/g and coercivity of 4.1747 and 5.1233 G, respectively, at 300 K. The magnetic properties are tabulated in Table 2. The saturation magnetization of pure Fe₃O₄ is lower than the value reported in the literature (92 emu/g).¹³ The samples show typical superparamagnetic behavior, with near zero coercivity and remanent magnetization, whereas pure HAp does not have any hysteresis loop. It is also clear from vibrating sample magnetometry that the magnetite particle in the composite structure is well within the single domain particle range and exhibits superparamagnetism. The magnetization value of the composites was lower than that of the pure Fe₃O₄ nanoparticles. The decreased saturation magnetization could be due to interaction between the iron core and the HAp shell, which decreases the magnetic moment.^14,15

Table 2 Magnetic properties of Fe₃O₄ and Fe₃O₄-HAp nanoparticles

Sample	Coercivity (G)	Saturation magnetization (emu/g)	Remanent magnetization (G)
Fe3O4 nanoparticle	4.1747	20.639	0
Fe3O4 -HAp nanocomposite	5.1233	7.34	0

Abbreviations: Fe₃O₄, iron oxide; HAp, hydroxyapatite.

Figure 5 Magnetic hysteresis loops of pure Fe₃O₄ and Fe₃O₄-HAp nanoparticles.

Abbreviations: Fe₃O₄, iron oxide; HAp, hydroxyapatite; NPs, nanoparticles; M_s, saturation magnetization.

Cytotoxicity testing

In vitro cytotoxicity assays are the primary biocompatibility screening tests for a wide variety of materials used in the medical field. The MTT assay was done for the Fe₃O₄ and Fe₃O₄-HAp nanoparticles using MG63 (osteosarcoma) cells. Three concentrations (1, 3, and 5 mg/mL) of the Fe₃O₄ nanoparticles and the Fe₃O₄-HAp nanocomposites were tested. The experiments were performed in triplicate. The mean values obtained are shown in Figure 6. The MTT assay procedure is explained in the flow chart given in Figure 2. The results show that the Fe₃O₄-HAp nanoparticles enabled better cell proliferation than the pure Fe₃O₄ at the concentrations tested.

Figure 6 Cytotoxicity test for pure Fe₃O₄ and Fe₃O₄-HAp nanoparticles.

Abbreviations: Fe₃O₄, iron oxide; HAp, hydroxyapatite.

Magnetic induction hyperthermia is a technique that can be used to destroy cancer cells via their hysteresis loss when placed in an alternating magnetic field. The prepared nanocomposites have the capacity to generate heat in the presence of an alternating magnetic field. The temperature of the cancer cells is raised between 42°C and 46°C via the heat produced by our prepared composite materials. Although the heating efficiency of the prepared superparamagnetic Fe₃O₄-HAp nanocomposite is not demonstrated here, Hou et al¹⁶ showed that a similar Fe₃O₄-HAp nanocomposite was capable of magnetically inducing effective thermal destruction of cancer cells in vivo.

Conclusion

In this work, pure Fe₃O₄ was prepared by alkaline coprecipitation and HAp nanoparticles were prepared using an optimized sol-gel method. Fe₃O₄-HAp (0.7 w/w) nanocomposites were developed by wet milling. The prepared Fe₃O₄-HAp nanoparticles and its composite were characterized and confirmed by scanning electron microscopy, Fourier transform infrared spectroscopy, and diffuse reflectance spectroscopy. Their superparamagnetic nature was confirmed by vibrating sample magnetometry, and their thermal stability was confirmed by thermogravimetric analysis and differential scanning calorimetry. This nanostructured Fe₃O₄-HAp composite would be ideal for use in bone cancer therapy.

Acknowledgments

The authors are grateful to their head of department, dean, principal, and management for providing the facilities to carry out this research. MS is grateful to TEQIP-II for providing a PhD research assistantship. This work was financially supported by DST (SB/S2/CMP-106/2013), New Delhi, and UGC (major, 42-907/2013SR), New Delhi.

Disclosure

The authors report no conflicts of interest in this work.