Evaluation of surface roughness and bond strength of quartz fiber posts after various pre-treatments

Abstract

Purpose. Debonding at the post-adhesive interface is a major problem for quartz fiber posts. The objective of this study was to evaluate surface roughness and bond strength of quartz fiber posts after various surface treatments. Materials and methods. Sixty-six quartz fiber posts were randomly divided into six experimental groups (n = 11) including group C, untreated (control); group SB, sandblasted; group SC, silica coated; group HF, hydrofluoric acid-etched; group N, Nd:YAG laser irradiated; group E, Er:YAG laser irradiated. Surface roughness of the posts was measured before and after pre-treatment. They were then bonded to resin cement and tensile bond strength was determined in a universal testing machine. Furthermore, two-way ANOVA and post hoc comparison tests (α = 0.05) were performed on all data. Results. The highest mean force value was observed in group SB and followed by group E. Tukey’s HSD test showed that there was no statistical difference between group SB and group E (p = 0.673). The highest mean roughness value was observed in group SB and a significant difference was found between group SB and all other groups (p < 0.001). This study reveals that sandblasting and Er:YAG laser irradiation provided a significant increase in bond strength between quartz fiber posts and resin cement. Conclusions. Sandblasting or Er:YAG laser-irradiation of the surface of the quartz fiber post before cementation is recommended for increasing retention.

Key Words::

• acid-etch
• bond strength
• laser
• quartz fiber post
• sandblasting
• silica coating

Acknowledgments

This investigation was supported by the Cumhuriyet University Scientific Research Project. This study was presented in a poster at the annual meeting of the 19th Aegean Region Chambers of Dentists International Scientific Congress and Exhibition, 26–28 April, 2012, Fethiye, Turkey.

Declaration of interest: The authors report no conflicts of interest. The authors alone are responsible for the content and writing of the paper.