A novel chitosan 3-amino-1,2,4-triazole hybrid: Preparation and its effects on cotton fabric propertiesFootnote

, &
Pages 768-774 | Received 27 Apr 2016, Accepted 13 Aug 2016, Published online: 16 Apr 2018
 

Abstract

A hybrid of chitosan and 3-amino-1,2,4-triazole was prepared using the semi-wet method, which allows for the adsorption of the triazole molecules on the chitosan surface. Moreover, an easy method for applying this hybrid to cotton fabric was established. The tensional strength, uniformity and compatibility of the hybrid components in forming of a strong film were studied using different variables, including the chitosan 3-amino-1,2,4-triazole ratio, fixation temperature and time. The loading of the hybrid onto the fabric in the absence and presence of cross linker (butane tetra carboxylic acid) was also studied. The best conditions for preparing the hybrid was a 1:4 molar ratio of chitosan to 3-amino-1,2,4-triazole at 60 °C for 240 min, and those for the application of the hybrid to cotton fabric were a 1:1 molar ratio at 150 °C with a 5 min curing time. Both hybrid and treated cotton fabrics were characterized using FTIR, SEM, TGA, and DSC as well as the nitrogen content and tensional strength of the treated cotton. Finally, the antibacterial activities of the treated cotton fabric display 100% activity and excellent effects against gram-positive bacteria, Staphylococcus aureus and gram-negative Escherichia coli.

Acknowledgements

The authors gratefully acknowledge Deanship of Scientific Research of Taibah University for the research funding (1434/4626) that supported this work.

Notes

Peer review under responsibility of Taibah University.