Direction of shrinkage of light-curing resin composites

Abstract

It is occasionally stated in the dental literature that light-curing resin composites shrink towards the light source. As light travels at the speed of light, this dictum is not obvious. It was the purpose of the present study to investigate the direction of shrinkage of a light-curing resin composite in relation to the attachment and the thickness of the material. The resin composite was applied in cylindrical brass molds in such a manner that a flash, serving as attachment, was produced at one side of the specimens, while the material was flush with the mold at the other side. The specimens were now irradiated from either the flash or the flush side, and the convexity or the concavity of the specimens was measured. At a material thickness of 3 mm, the shrinkage was towards the light source, irrespective of the position of the flash. At 4 and 5 mm thickness of the molds, the direction of shrinkage could be directed towards or away from the light source, depending on the position of the flash. The number of light quanta emitted from the light source and passing through the material was compared with the number of molecules of camphorquinone present in a resin composite of 3, 4, or 5 mm thickness. It was concluded that under the conditions of the present study, the direction of shrinkage was the result of an interplay between the direction of the light, the attachment of the material, and the thickness of the material.