The Identification of Heat Strengthened Glass in Windshields

ABSTRACT

An unusually large change in refractive index after re-annealing (ΔRI), 0.00106, was observed in a sample of windshield glass submitted in a case. The manufacturer of this windshield indicates that a minority of windshields is produced by the press bend method and that this results in glass with higher stress than is normal in non-tempered glass. Known samples of press bend glass were also found to have a similarly large ΔRI after re-annealing. A total of 94 samples of windshield glass were examined with 83 found to have a ΔRI in the normal range for non-tempered glass and 11 having a ΔRI above this range. This is a previously unreported property by which windshield glass can be classified by forensic scientists.

RÉSUMÉ

Un changement de l'indice de réfraction plus grand que normal a été observé après la recuisson (ΔRI) d'un échantillon de verre provenant d'un pare-brise soumis dans une cause. Le fabricant de ce pare-brise a indiqué qu'une minorité de pare-brise sont produits par la méthode du bombage par emboutissage et que ceci donne un verre ayant plus de contraintes que ce qui est normal pour le verre non-trempé. On a observé que des échantillons connus de verre produits par la méthode du bombage par emboutissage avaient aussi un plus grand ARI que normal après la recuisson. Un total de 94 échantillons de verre provenant de pare-brise ont été examinés. De ces 94 échantillons, 83 avaient un ΔRI dans les limites normales pour du verre non-trempé et 11 avaient un ΔRI au-dessus de ces limites. Ceci est une propriété qui n'a jamais été signalée auparavant et par laquelle le verre de pare-brise peut être classifié par les scientifiques judiciaires.