The Effect of Added Al2O3 on the Propagation Behavior of an Al/CuO Nanoscale Thermite

, , &
Pages 1278-1294 | Received 16 Jan 2007, Accepted 19 Dec 2007, Published online: 12 Jun 2008
 

Abstract

Three types of experiments were performed on an Al/CuO nanoscale thermite to understand the effect of adding a diluent (40 nm Al2O3 particles) to the mixture: the constant volume pressure cell, the unconfined burn tray, and the instrumented burn tube. The addition of Al2O3 decreased the pressure output and reaction velocity in all three experiments. Burn tube measurements showed three reaction velocity regimes: constant velocity observed when 0% (633 m/s) and 5% (570 m/s) of the total weight is Al2O3, constant acceleration observed at 10% (146 m/s to 544 m/s over a distance of 6 cm) and 15% (69 m/s to 112 m/s over a distance of 6 cm) Al2O3, and an unstable, spiraling combustion wave at 20% Al2O3. The pressure measurements correlated to these three regimes showing a dropoff in peak pressure as Al2O3 was added to the system, with relatively no pressure increase observed when 20% of the total weight was Al2O3. Equilibrium calculations showed that the addition of Al2O3 to an Al/CuO mixture lowered the flame temperature, reducing the amount of combustion products in the gas phase, thus, hindering the presumed primary mode of forward heat transfer, convection.

Authors are supported by Los Alamos National Laboratory (LANL), which is operated for the U.S. Department of Energy under the contract DE-AC52-06NA25396. Work was supported by the Joint DoD/DOE Munitions Program under the supervision of Sherri Bingert and the U.S. Army Research Office under the Multi-University Research Initiative under Contract No. W911NF-04-1-0178. The authors give a special thank you to Adam Pacheco and Dave Oschwald for their help setting up and running the equipment that made this study possible. For his help interpreting pressure transducer results, Dr. Patrick Walter of Texas Christian University is thanked as well. This work has been assigned LA-UR #07-7888.

Reprints and Corporate Permissions

Please note: Selecting permissions does not provide access to the full text of the article, please see our help page How do I view content?

To request a reprint or corporate permissions for this article, please click on the relevant link below:

Academic Permissions

Please note: Selecting permissions does not provide access to the full text of the article, please see our help page How do I view content?

Obtain permissions instantly via Rightslink by clicking on the button below:

If you are unable to obtain permissions via Rightslink, please complete and submit this Permissions form. For more information, please visit our Permissions help page.