Abstract
The compositions of 0.9SrTiO 3 -0.1TiO2 with 0–8wt% Borosilicate glass additive were prepared. The microstructures and dielectric properties of the sintered bodies were studied. It was found a tiny amount of glass additive could lower the sintering temperature of the ceramics, and a very dense microstructure with fine grains was obtained, which resulted in higher dielectric constant and higher breakdown strength (BDS). However, As Borosilicate glass content increased, SrTiO3 had a tendency to react with the glass phase resulting in the productions of SrAl2Si2O8 and TiO2, which had a negative influence on the microstructures of ceramics, consequently degraded the dielectric properties.