Abstract
The crystalline structure and dielectric properties of nominal Sm 1.75 Sr 0.25 NiO 4 ceramics are presented. Three phases, Sm 1.70 Sr 0.30 NiO 4 , Sm 2 O 3 and NiO, are found in the present ceramics, and the abundances are 77.7(1.1) wt%, 19.2(3) wt% and 6.1(2) wt%, respectively. The temperature-stable giant dielectric constant over 60 000 even up to 5 MHz is observed in a broad temperature range. The modulus plots show that the giant dielectric constant should be originated from the contribution of the grain interior instead of grain boundary. Compared with the other giant dielectric constant materials, the present materials have the great potentiality in the practical application, especially for the high frequency application.