Effect of Adhesive Thickness on Joint Strength: A Molecular Dynamics Perspective

Abstract

Recent studies suggest that adhesion in thin joints depends on several factors including temperature, interface toughness, strain rate, surface roughness of adherends, bondline thickness of adhesives, and many others. Influence of thickness on joint properties is surprising but experimentally well documented without reasonable explanations. In this study, we attempt to address the mechanical behavior of polymer adhesives by molecular dynamics (MD) simulation. We show that interfacial strength of the joints in tensile, shear, or combined loading significantly depends on the coupling strength between adhesives and adherends. Failure of joints is always at the interface when coupling strength is weaker. With stronger interfaces, cohesive failure occurs by cavitation or by bulk shear depending on the loading condition. When joints are loaded in tension, it requires an exceedingly stronger interface to realize pure shear failure, otherwise failure is through interface slip. Under a mixed mode condition, interface slip is difficult to avoid. As long as failure is not at the interface alone, the yield strength of joints improves significantly with the reduction of thickness. Increase in bulk density and change in polymer configurations with the reduction of adhesive thickness are believed to be the two key factors in improving mechanical behavior of adhesives.

Keywords:

• Adhesive thickness
• Failure
• Interface strength
• Molecular dynamics
• Shear
• Tensile

ACKNOWLEDGMENT

This work was supported by a National Science Foundation Grant No. HRD-976871.