Phase transformations and structural characteristics of AL–Cu–Co(–Si) decagonal phase

Abstract

The phase transformations and structural characteristics of the Al-Cu-Co-Si alloy have been studied by neutron diffraction and high-resolution electron microscopy. The Al₆₅Cu_17.5Co_17.5 decagonal phase is stable in the temperature range between 973 K and 1350 K. At the low-temperature end, it relaxes to a microcrystalline approximant structure. At the high-temperature end, it melts directly into liquid. Two distinct orthorhombic phases are identified in the Al₆₃Cu_17.5Co_17.5Si₂ microcrystalline structure. They are composed of several structure units that can also construct the Penrose tiling. Because of lack of units, a single orthorhombic phase cannot undergo the transformation towards the high-temperature decagonal phase. An analysis of the orientation relationships between the CsCl and orthorhombic phases leads to the definition of Penrose tiling-like subnetworks inside the orthorhombic unit cells so that these orthorhombic phases can be regarded as the periodic patchworks of quasiperiodic subnetworks.

Key Words:

• Quasicrystal
• neutron diffraction
• phase transitions
• electron microscopy
• intermetallic compounds