Abstract
The movement of grain boundary dislocations in a recrystallizing boundary in aluminium has been shown by the observation of oblique slip traces left behind a migrating interface. This indicates that the moving grain boundary retains the structure of the stationary boundary. The observed movement cannot, however, completely account for the migration using a dislocation mechanism for migration.