Abstract
The apparent conflict between two experimental estimates of the Peierls stress in fcc metals, σB from Bordoni peak experiments and σf from low-temperature plastic flow measurements, is settled within the standard Peierls model of dislocation dynamics. We prove that the Peierls stress is estimated correctly by σB, the ratio σf/σB being proportional to the (small) dislocation damping constant.