Effect of adhesive application on the shear bond strength of refrigerated and pre-heated of different composite resins to orthodontic molar tubes

Abstract

Objective: To evaluate the effect of adhesive application on the shear bond strength (SBS) of orthodontic tubes to acid-etched human enamel using different temperatures and orthodontic composite resins. Methods: One hundred and twenty metal tubes were bonded to human third molars, which were randomly divided into three groups depending on the composite used: Transbond XT (XT); Transbond Supreme LV (LV); and Light Bond (LB). Each group was divided into four subgroups depending on the temperature (5°, 20°, 40°, and 60°) applied to the composite before cementing. For each experimental subgroup, half the specimens were bonded in combination with XT Primer. After 72 h, a SBS test was performed using a universal testing machine. Statistical analysis was performed using ANOVA, post hoc intergroup comparisons, chi-square test, and linear regression. Two representative molar surfaces from each subgroup were assessed under Scanning electron microscope. Results: The composite type only influenced XT regarding LB. The use of adhesive does not affect the SBS values of any composite. The flowable composites with adhesive containing zirconia (LV) as a filler showed lower SBS when cooled to 5 °C and when increases the temperature from 40 °C. Whether adhesive was used or not, composites with silica as filler (LB) showed lower SBS at 60 °C and increased to 5 °C. Conclusions: For all composites, from 20 °C, SBS values tend to increased and started to decline at 40°C except when adhesive is applied to the quartz-filled composite, which continues to increase, and the silica-filled composite without adhesive, which tend to decreases from 5 °C.

Keywords:

• pre-heated composite
• refrigerated composite
• shear bond strength
• adhesive
• molar tube