Mechanical properties of carbon fiber composites modified with nano-SiO₂ in the interphase

Abstract

The performance of carbon fibers-reinforced composites is dependent to a great extent on the properties of fiber–matrix interface. To improve the interfacial properties in carbon fibers/epoxy composites, nano-SiO₂ particles were introduced to the surface of carbon fibers by sizing treatment. Atomic force microscope (AFM) results showed that nano-SiO₂ particles had been introduced on the surface of carbon fibers and increase the surface roughness of carbon fibers. X-ray photoelectron spectroscopy (XPS) showed that nano-SiO₂ particles increased the content of oxygen-containing groups on carbon fibers surface. Single fiber pull-out test (IFSS) and short-beam bending test (ILSS) results showed that the IFSS and ILSS of carbon fibers/epoxy composites could obtain 30.8 and 10.6% improvement compared with the composites without nano-SiO₂, respectively, when the nano-SiO₂ content was 1 wt % in sizing agents. Impact test of carbon fibers/epoxy composites treated by nano-SiO₂ containing sizing showed higher absorption energy than that of carbon fibers/epoxy composites treated by sizing agent without nano-SiO₂. Scanning electron microscopy (SEM) of impact fracture surface showed that the interfacial adhesion between fibers and matrix was improved after nano-SiO₂-modified sizing treatment. Dynamic mechanical thermal analysis (DMTA) showed that the introduction of nano-SiO₂ to carbon fibers surface effectively improved the storage modulus of carbon fibers/epoxy.

Keywords:

• carbon fiber
• sizing agent
• mechanical properties
• composites
• surfaces

Additional information

Funding

Funding. This work was financially supported by the National High Technology Research and Development Program of China [863 Program, grant number 2012AA03A212].