Abstract
The aim of the present study was to investigate the effects of three different surface treatments and two different adhesives on the microtensile bond strength (μTBS) of repaired composites using the same or different type of resin. Twenty-four nano-hybrid (Ceram X mono-C) and 24 nanofilled (Filtek Ultimate-F) composite discs were prepared. The specimens were aged with 5000 thermocycles and randomly divided into groups according to the surface treatment methods: (a) phosphoric acid (b) Er:YAG laser and (c) aluminum trioxide particle (air abrasion). Fresh composite resins (C and F) were added to the treated surfaces with two different adhesives (two-step and one-step self-etch adhesives). Then, the specimens were aged again. The stick-shaped specimens were prepared from the discs (n = 25) and the sticks were subjected to the μTBS test. Results indicated that significant differences were found in μTBS values among the surface treatment methods. In the C groups, the highest μTBS value (41.3 ± 8.3 MPa) was recorded in the air abrasion and one-step self-etch adhesive group, which were repaired with the same kind of composite. In the F groups, the highest μTBS value was observed in the air abrasion and one-step self-etch adhesive (37.6 ± 12.3 MPa) group. The treatment with air abrasion is more effective than the others, and it may be suggested for composite repair.
Acknowledgements
The authors would like to thanks 3M ESPE Dental Products Manufacturer for contribution the products used in this study.
Disclosure statement
No potential conflict of interest was reported by the authors.