Effects of polymer, organic solvent and mixing strength on integrity of proteins and liposomes encapsulated in polymeric microspheres fabricated by the double emulsion process

, &
Pages 399-412 | Received 01 May 2003, Accepted 24 Jan 2004, Published online: 03 Oct 2008
 

Abstract

The double emulsion process has commonly been applied to encapsulate water-soluble bioactive agents into polymeric microspheres. However, the integrity of many of these agents may be destroyed by the highly energetic procedures such as sonication that are routinely used to produce stable water-in-oil (w/o) emulsion. The aim of this research was to pursue the possibility of replacing the sonication by a mild emulsification procedure such as vortex mixing, with the use of certain materials to help to obtain stable w/o emulsion. The following materials were examined: poly(lactide-co-ethylene glycol) (PELA) as the polymer, ethyl acetate and acetone as the solvents, poly(vinyl alcohol) (PVA) and d-α tocopheryl polyethylene glycol 1000 succinate (Vitamin E TPGS) as the emulsifiers in w/o emulsion. The experimental results, with human serum albumin (HSA) as the encapsulated agent, showed that, when vortex mixing was used, these materials could significantly improve w/o emulsion stability and help to obtain satisfactory encapsulation effects, i.e. high encapsulation efficiency (EE) and low initial release burst. A delicate structure, i.e. liposomes, which is very sensitive to sonication, was then incorporated into microspheres by the ‘modified double emulsion process’. It was found that the liposomes were intact and the encapsulation effects were good. Therefore, it can be concluded that the modified double emulsion process could be advantageous for the encapsulation of delicate substances.

Reprints and Corporate Permissions

Please note: Selecting permissions does not provide access to the full text of the article, please see our help page How do I view content?

To request a reprint or corporate permissions for this article, please click on the relevant link below:

Academic Permissions

Please note: Selecting permissions does not provide access to the full text of the article, please see our help page How do I view content?

Obtain permissions instantly via Rightslink by clicking on the button below:

If you are unable to obtain permissions via Rightslink, please complete and submit this Permissions form. For more information, please visit our Permissions help page.