Microstructure and corrosion behaviour of WC/NiCrBSi coatings by vacuum cladding

Abstract

In this work, the WC-NiCrBSi and in-situ synthesised WC (IWC)-NiCrBSi coatings were successfully fabricated on SS 316 L using vacuum cladding process to investigate the WC-reinforced NiCrBSi alloy by the two methods. XRD, SEM and EDS were performed to characterise the phase constituents, microstructure and chemical composition, respectively. Subsequently, electrochemical corrosion and cavitation tests of the coatings were carried out in 3.5 wt-% NaCl solution. The results showed that the WC-NiCrBSi cladding coating was mainly composed of γ-Ni, FeNi₃, WC, Cr₂₃C₆ and CrB phases, while the IWC-NiCrBSi cladding coating was composed of γ-Ni, WC, FeNi₃, Cr₂₃C₆, Cr₇C₃, CrB phases. The corrosion current density of the WC-NiCrBSi and IWC-NiCrBSi coatings were 5.01 × 10⁻⁷ and 3.57 × 10⁻⁷ A/cm², respectively. The combined analysis of cumulative weight loss curve and cavitation morphology revealed a better cavitation resistance by the IWC-NiCrBSi coating than the WC-NiCrBSi coating in 3.5 wt-% NaCl solution.

KEYWORDS:

• Vacuum cladding
• WC/NiCrBSi coating
• corrosion behaviour

Acknowledgements

The authors gratefully acknowledge to the financial support for this research from National Key Research and Development Program of China (No. 2016YFB1100204), Key Research Project from Shenyang Science and Technology Funded Project (Nos. 19-109-1-03).

Disclosure statement

No potential conflict of interest was reported by the author(s).

Data availability statement

The raw/processed data required to reproduce these findings cannot be shared at this time as the data also forms part of a continuing study.

Additional information

Funding

This work was supported by Key Research Project from Shenyang Science and Technology Funded Project: [grant number 19-109-1-03]; National Key Research and Development Program of China: [grant number 2016YFB1100204].