Polymer nanostructure development of fluorinated and aliphatic monoacrylates in smectic liquid crystals via photopolymerization

Abstract

To develop viable polymer stabilized liquid crystal systems, it is crucial to understand the factors that affect polymer nanostructure evolution. This work examines the influence of the photopolymerization of aliphatic and fluorinated monoacrylate monomer within a room temperature smectic liquid crystal (LC). Additionally, the effect of LC order on polymerization kinetics, monomer and polymer organization, and the effect of the polymer on LC properties have been examined. Through this work, insight has been gained regarding the impact that the introduction of a fluorinated monoacrylate monomer has on polymerization kinetics, LC organization, and monomer/polymer segregation and organization within a polymer/LC system. Fluorinated moieties lower the surface energy of the monomer to enhance segregation between the smectic layers of the LC as compared with an analogous aliphatic monomer. Additionally, the enhanced segregation significantly increases the polymerization rate in the smectic phase and drives the continued segregation of the fluorinated polymer during and after polymerization. Fluorination also leads to the formation of an ordered polymer nanostructure if polymerized in ordered LC phases. This ordering is particularly evident when the fluorinated monomer is polymerized in the smectic phase in which the monomer is organized between the smectic layers of the LC. In addition, the ordered polymer structure found with the fluorinated monomer in the smectic phase leads to continued birefringence above the clearing point of the LC due to surface interactions between the LC and the ordered fluorinated polymer. The continued birefringence offers an exceptional opportunity to examine how factors such as polymer molecular mass and UV light intensity affect the overall polymer morphology of these polymer/LC systems. As the initiator concentration and UV light intensity are decreased, longer polymer chains form lattice-type morphologies; whereas, shorter polymer chains form smoother morphologies that more closely mirror the texture of the LC smectic phase.