Morphological phase behaviour under pressure of polycatenar mesogens with a perfluorinated moiety

Abstract

Two polycatenar materials composed of a four‐aromatic‐ring core with a perfluorinated moiety attached in one terminal position through either butylene‐ or pentylene spacer groups, and three tetradecyloxy chains at the other end (abbreviated as 14PC₄F and 14PC₅F), were investigated to study the effect of pressure on the phase transition behaviour. A polarizing optical microscope equipped with a high pressure optical hot stage, was used for the purpose. The T vs. P phase diagrams of 14PC₄F and 14PC₅F were constructed in the pressure region up to 100 MPa. 14PC₄F showed the stable crystal (Cr₁)–columnar tetragonal (Col_tet)–smectic A (SmA)–columnar hexagonal (Col_h)–isoropic liquid (I) phase transition sequence under all pressures. 14PC₅F exhibited the phase sequence metastable crystal (Cr₂)–cubic (Cub)–Col_tet–SmA–I in a melt‐cooled sample on heating under pressure. But when the melt‐cooled Cr₂ sample was annealed at 52–54°C for 2–3 h, the stable crystal (Cr₁) was formed slowly, giving a stable Cr₁–Cub–Col_tet–SmA–I phase sequence. The temperature region of the stable cubic phase broadened with increasing pressure. Furthermore a new mesophase of 14PC₅F was pressure‐induced between the I and SmA phases on cooling at pressures above about 16 MPa. Since the monotropic mesophase exhibited a texture very similar to that of the high temperature Col_h phase of 14PC₄F with planar orientation, the new phase was assigned at a high temperature columnar hexagonal phase of 14PC₅F.