Liquid crystalline polymers XII. Main chain thermotropic poly(arylidene-ether)s containing 4-tertiary-butyl-cyclohexanone moiety linked with polymethylene spacers

Abstract

A new homologous series of thermally stable thermotropic liquid crystalline poly(arylidene-ether)s based on 4-tertiary-butyl-cyclohexanone moiety was synthesised by solution polycondensation of 4,4′-diformyl-α,ω-diphenoxyalkanes, I_a–f, or 4,4′-diformyl-2,2′-dimethoxy-α,ω-diphenoxyalkanes, II_a–f, with the 4-tertiary-butyl-cyclohexanone monomer. A model compound III was synthesised from the monomer with benzaldehyde and characterised by elemental and spectral analyses. The inherent viscosities of the resulting polymers were in the range of 0.18–0.92 dL/g. The mesomorphic properties of these polymers were studied as a function of the diphenoxyalkane space length. Their thermotropic liquid crystalline properties were examined by differential scanning calorimetry (DSC) and optical polarising microscopy and demonstrated that the resulting polymers form nematic mesophases over wide temperature ranges. The thermal properties of those polymers were evaluated by thermogravimetric analysis and DSC measurements and correlated to their structural units. X-ray analysis showed that polymers having some degree of crystallinity in the region 2θ = 5–60°. In addition, the morphological properties of selected examples were tested by scanning electron microscopy.

Keywords:

• liquid crystasls
• thermotropic
• synthesis
• characterisation
• poly(arylidene-ether)s