The chitosan/starch blend films of 2:1 ratio were prepared by solution casting. Tensile strength (TS) and elongation at break (%Eb) of chitosan/starch blend film were found to be 9.33 MPa and 3.6%, respectively. The blend films (2% Chitosan) were soaked in six different formulations of methylmethacrylate (MMA) monomer and aliphatic urethane diacrylate oligomer (M-1200) at different time intervals (1–5 min) and irradiated under UV radiation at different intensities (5–35 pass). Formulations containing 43% MMA and 15% oligomer in methanol solution showed 209% increase in TS at 25th UV pass for 4 min soaking time. SEM and FTIR were used to investigate the molecular interaction and morphology of the blend film, respectively.