Friction and Wear Behavior of Single-Crystal Silicon Carbide in Sliding Contact with Various Metals

Abstract

Sliding friction experiments were conducted with single-crystal silicon carbide in contact with various metals. Results indicate the coefficient of friction is related to the relative chemical activity of the metals. The more active the metal, the higher the coefficient of friction. All the metals examined transferred to silicon carbide. The chemical activity of the metal and its shear modulus may play important roles in metal-transfer, the form of the wear debris and the surface roughness of the metal wear scar. The more active the metal, and the less resistance to shear, the greater the transfer to silicon carbide and the rougher the wear scar on the surface of the metal. Hexagon-shaped cracking and fracturing formed by cleavage of both prismatic and basal planes is observed on the silicon carbide surface.

Presented at the 33rd Annual Meeting in Dearborn, Michigan, April 17–20, 1978

Notes

Presented at the 33rd Annual Meeting in Dearborn, Michigan, April 17–20, 1978