Abstract
Energy Dispersive X-ray Diffraction (EDXD) was performed at room temperature to gather structural data on CaS between approximately 1.7 GPa to nearly 150GPa. In these experiments, CaS retained the B1 structure up to approximately 40 GPa above which it began to transform to the B2 structure. The B2 structure remained stable to the highest pressure reached, 149 GPa, where the relative volume V/V0 was 0.490. Previous studies on CaS extended only up to 52 GPa, which is barely 10 GPa after the B1 phase changes to the B2 structure. Thus it was not possible to accurately extrapolate the equation of state (EOS) for the B2 phase region to significantly higher pressures. In the present study EOS data for CaS was collected to 150 GPa and no other structural change was observed. EOS parameters for the B1 and B2 phase regions agree well with values reported in the literature.