Solidification of selenium melt under pressure up to 6.5 GPa

Abstract

High purity selenium samples were melted under high pressure (≤6.4 GPa) and quenched at various rates ranging from 2 K s⁻¹ to 500 K s⁻¹ and the recovered material was examined by X-ray diffraction and electron microscopy. In the entire range of pressure and cooling rate, the melt was found to solidify into a polycrystalline aggregate of the trigonal phase of selenium. The samples obtained by slow cooling of the melt at 6.4 GPa contain, in addition to crystalline phase, regions which appear to be amorphous.