Abstract
Amorphous, ferromagnetic, invar like, Fe60 Mn20 B20 alloy has been investigated. Two kinds of experiments were carried out for this alloy. The first, using high pressure technique, revealed the influence of pressure on B(H) dependencies within the wide range of temperature under pressure of 0.5 GPa. From the magnetization curves obtained during these experiments the decrease of spontaneous magnetization caused by applied pressure 0.5 GPa at temperature -180°C has been calculated at the rate about 7 10−11T/Pa.
In the second kind of experiments the measurements of volume magnetostriction up to 720 kA/m magnetic field intensity have been done. Volume magnetostriction coefficient at temperature 77.4 K has been determined to be about 2 10−11 [A/m]−1.