New polymorphs of alumina

Abstract

We present the results of high-pressure, high-temperature studies on xerogel gamma alumina which is made up of nanocrystalline alumina and an amorphous phase. Not many studies of this type have been reported on xerogel materials. At about 5 GPa and 1400°C, the xerogel alumina transforms into a polymorphic mixture containing α Al₂O₃, B Al₂O₃ and C Al₂O₃ where the last two phases have B Ln₂O₃ and C Ln₂O₃ type structures respectively. Here Ln stands for the rare earths. The xerogel alumina containing 1 wt.% Cr₂O₃ under these conditions transforms into a polymorphic mixture containing Al₂O₃, k' Al₂O₃ and H Al₂O₃ where H Al₂O₃ has the H Ln₂O₃ type structure. For the first time, the observation of rare earth sesquioxide structures of alumina is reported. At about 5 GPa at 27°C, the xerogel aluminal transforms to an amorphous phase. The results are discussed using the free energy diagram for xerogels proposed by R. Roy (J. Amer. Cer. Soc., 52, 344, 1969; 67, 468, 1984).

Key Words:

• Alumina
• nanocrystalline phase
• high pressure/temperature