Intrinsic deformation properties of icosahedral Al-Pd-Mn single quasicrystals

Abstract

Plastic deformation experiments were performed on icosahedral Al-Pd-Mn single-quasicrystals to determine the thermodynamic activation parameters of the deformation process. The stress exponent and the strain-rate sensitivity of the flow stress were obtained by means of stress relaxation experiments. The activation enthalpy of the deformation process was measured by temperature change experiments. In the range from 730 to 800°C a nearly constant value of about 7 eV was determined.