The influence of positive polarity time on GTAW AC of aluminium

&
Pages 825-833 | Received 25 Sep 2008, Accepted 24 May 2009, Published online: 11 Oct 2010
 

Abstract

In this work, experiments were carried out to determine the welding behaviour of aluminium 1200 based on an increase in the activation time of the positive polarity for tungsten inert gas AC welding of this metal. To achieve this objective, a series of experiments was developed, in such a way that the intensity of the electrical current in the positive and negative polarities was the same; only the duration times in each polarity were modified. During the experiments, the current and voltage signals were acquired. In this way, the arc voltage and potential could be determined for each condition tested. In terms of the fusion behaviour, an increase in penetration and in welded areas was verified to the extent that longer positive polarity times were used. This behaviour is different from that commonly indicated in the literature about welding processes with non-consumable electrodes, which suggests a reduction in penetration with an increase in the positive polarity activation time. However, this trend grows constantly during the experiments from a determined point, where the positive polarity activity times are greater than 4.0 ms in a total period of 20.0 ms. The use of a minimum positive polarity time (1.3 ms) was shown to be effective for cathode cleaning, as it produced welds with satisfactory fusion characteristics and with minimum wear to the tungsten electrode. The good fusion capacity obtained in welds produced with long positive polarity times was attributed to phenomena arising from the emission of electrons due to the field effect that occurs during the positive electrode phases.

Acknowledgements

We thank the whole team at LABSOLDA and in particular to Ricardo Campagnin, Hellinton Direne, Ivan Pigozzo, Marcelo Okuyama and Tiago Vieira for their support to this work.

Notes

Additional information

Notes on contributors

Luciano Machado Cirino

1 1. [email protected]

Jair Carlos Dutra

2 2. [email protected]

Reprints and Corporate Permissions

Please note: Selecting permissions does not provide access to the full text of the article, please see our help page How do I view content?

To request a reprint or corporate permissions for this article, please click on the relevant link below:

Academic Permissions

Please note: Selecting permissions does not provide access to the full text of the article, please see our help page How do I view content?

Obtain permissions instantly via Rightslink by clicking on the button below:

If you are unable to obtain permissions via Rightslink, please complete and submit this Permissions form. For more information, please visit our Permissions help page.