Microstructure evaluation and mechanical properties of a friction stir spot welded TRIP 800 steel

, , , , , , & show all
Pages 683-690 | Received 07 Dec 2008, Accepted 09 Nov 2009, Published online: 15 Aug 2011
 

Abstract

A TRIP 800 steel was friction stir spot welded using three different tool rotational speeds, 1600, 2000 and 2400 rpm, and the dwell time was kept constant at 2 s. The resultant microstructures formed in each weld zone were analysed as well as their hardness. Higher hardness values were observed for the lowest rotational speed, 1600 rpm, where the heat input in theory was lower and, therefore, the cooling rate was faster. However, for this rotational speed, allotriomorphic ferrite was also observed in the stir zone. In the lap shear tests, samples welded at 1600 and 2400 rpm did not reach the minimum value recommended by the AWS D8.1M standard, which was attributed to the lower bonding ligament length and also lower distance between the keyhole left by the pin and the end of the zinc line, which is formed in the stir zone. The fracture of the samples occurred along this line. As a result, the influence of the microstructure on the failure process could only be inferred when the zinc line disappeared.

Acknowledgements

The authors would like to thank the financial support granted by CAPES and DAAD by way of the PROBAL Project set up between Brazil and Germany and to GKSS Forschungszentrum GmbH for the infrastructure provided. In addition to this, the authors thank the CNPq for the Doctorate grants awarded.

Notes

a. Mazda develops world's first aluminium joining technology using friction heat [cited 2007 Nov 9]. Available from: http://www.mazda.com/publicity/release/2003/200302/0227e.html.

Reprints and Corporate Permissions

Please note: Selecting permissions does not provide access to the full text of the article, please see our help page How do I view content?

To request a reprint or corporate permissions for this article, please click on the relevant link below:

Academic Permissions

Please note: Selecting permissions does not provide access to the full text of the article, please see our help page How do I view content?

Obtain permissions instantly via Rightslink by clicking on the button below:

If you are unable to obtain permissions via Rightslink, please complete and submit this Permissions form. For more information, please visit our Permissions help page.