Bead characterization of FCAW of a rutilic fluxed core wire

, &
Pages 825-837 | Published online: 22 Sep 2011
 

Abstract

This paper studies the effect of operational conditions on bead shape characteristics in fluxed core arc welding with a Brazilian-made wire with rutilic flux (ASME SFA-5.20: E71T-1/E71T-9/E71t-9M) of 1.2 mm in diameter. Bead-on-plate downhand welding trails were performed on 12 mm-thick low-carbon steel plates with a constant voltage power supply. A digital data logging system was used to measure the welding current and voltage, and wire feed rate. While the shielding gas composition (75% Ar–25% CO2 and 100% CO2), wire polarity, and feed rate (7 and 9 m/min) were varied during the trials, the electrode voltage (16 mm) and arc length (3.5 mm) were not changed. Weld bead characteristics (penetration depth, width, and fused and deposited areas), the presence of discontinuities, bead microstructure, and hardness were evaluated. Welding conditions of high productivity (high deposition rate) associated with adequate bead characteristics were determined for the wire.

Acknowledgements

The authors thank all who contributed to this paper. In particular, FAPEMIG for their financial support (concession of the Scientific Initiation Grant and finance via TEC-423/06 Project).

Notes

Additional information

Notes on contributors

Paulo J. Modenesi

1 1. [email protected]

Tadeu Messias Donizete Borba

2 2. [email protected]

Reprints and Corporate Permissions

Please note: Selecting permissions does not provide access to the full text of the article, please see our help page How do I view content?

To request a reprint or corporate permissions for this article, please click on the relevant link below:

Academic Permissions

Please note: Selecting permissions does not provide access to the full text of the article, please see our help page How do I view content?

Obtain permissions instantly via Rightslink by clicking on the button below:

If you are unable to obtain permissions via Rightslink, please complete and submit this Permissions form. For more information, please visit our Permissions help page.