The objective of this paper was to report the results of butt joint quality of friction stir welding (FSW) of samples of alloys of MgAlZn group. Welding has been carried out with the FSW tool of welding speed ranging from 140 to 355 mm/min. In the stir zone and the surrounding, neither porosity nor cracks have been obtained. Microhardness in the stir zone increased for all welds when compared to the base metals, as a consequence of the high grain refinement and increased precipitations at the grain boundaries. The decrease in plastic properties of metal in these regions is expected. The results show a strong relationship between properties of joints and welding parameters.