Influence of heat input on bead profile and microstructure characteristics in laser and laser-hybrid welding of Inconel 617 alloy

, &
Pages 256-270 | Received 24 Nov 2021, Accepted 03 Apr 2022, Published online: 22 Apr 2022
 

Abstract

Bead profile and microstructure analysis are greatly influenced by heat input in any welding process. The present work provides a comprehensive comparative investigation on these aspects during Autogenous Laser welding (ALW) and Laser-MIG Hybrid welding (LHW) processes in Inconel 617 superalloy. In case of LHW, weld bead profile formed was a typical wine-cup shaped one, whereas, in case of ALW, bead profile observed was Y-type shape on account of differences in number of heat sources and intensity profiles. Weld bead width and penetration depth were found to increase with heat input in both ALW and LHW processes. The fusion zone (FZ) area of LHW was found to increase by 3 times as compared to ALW as a result of high heat input in LHW than ALW. Indeed, the addition of MIG source to laser in LHW produced wide upper bead width (trebled) as compared to ALW. Radius of curvature (ROC) at neck zone, an important bead profile characteristic for assessing liquation cracking susceptibility, was found to increase with heat input and was significantly higher in LHW than ALW due to heat stagnation at neck zone. In comparison with ALW, LHW showed a coarser columnar/cellular dendritic microstructure in FZ with segregation of inter-dendritic carbides relatively richer in Mo and Cr. Secondary dendritic arm spacing (SDAS), cooling rates and microhardness will also be discussed.

Acknowledgements

The authors extend their thanks to Director, ARCI for granting permission to publish the work. We also acknowledge the experimental support provided by Mr K.V. Phani Prabhakar, Scientist, ARCI and Mr Anbu Rasu E, Technical Officer, ARCI. Authors would also like to thank DST-FIST and DST-PURSE grant for the FESEM-EDS facility and its maintenance at School of Engineering Science and Technology, University of Hyderabad.

Disclosure statement

No potential conflict of interest was reported by the author(s).

Additional information

Funding

Department of Science and Technology (DST), New Delhi is acknowledged for funding the project ‘National Centre for Development of Advanced Materials and Manufacturing Processes for Clean Coal Technologies for Power Applications’ (Program code. SNCD), under which this work was undertaken.

Reprints and Corporate Permissions

Please note: Selecting permissions does not provide access to the full text of the article, please see our help page How do I view content?

To request a reprint or corporate permissions for this article, please click on the relevant link below:

Academic Permissions

Please note: Selecting permissions does not provide access to the full text of the article, please see our help page How do I view content?

Obtain permissions instantly via Rightslink by clicking on the button below:

If you are unable to obtain permissions via Rightslink, please complete and submit this Permissions form. For more information, please visit our Permissions help page.