Abstract
Welding of two dissimilar alloys of aluminium such as AA5082 and AA6061 using friction stir welding (FSW) and their weldability has been studied in terms of microstructural and mechanical characteristics of the formed joint. Assessment of tensile strength of the weld joint and microhardness in the weld zone and the thermo-mechanically affected zone were done. The joint showed a tensile strength of 0.253 kN/mm2 and a Rockwell hardness of 54 HRA. Optical microscopy was conducted to study microstructure in different areas on the joined workpieces. Neither cracking nor porosity was observed in the weld zone in several high-resolution optical examinations, implying that defect free zones seem to have formed with the process parameters used, i.e. at 1000 RPM and 30 mm/min. This indicates a very good compatibility in welding the two alloys.
Acknowledgements
The authors thank Raghu Engineering College for providing their facilities and their continued encouragement to publish this work.
Disclosure statement
No potential conflict of interest was reported by the authors.
Data availability statement
The raw data available within this work are the data from various experiments conducted during the research and have been included in various forms within this paper itself. The raw/processed data required to reproduce these findings at this time also forms part of an ongoing study.