The Evaluation of a Modified Chrome Oxide Based High Temperature Solid Lubricant Coating for Foil Gas Bearings

Abstract

This paper describes the friction and wear performance of PS304, a modified chrome oxide based coating, for foil gas bearings. PS304 contains 60 wt. % NiCr binder, 20 wt. % Cr₂0₃ hardener, and 10 wt. % each Ag and BaF₂ICaF₂ lubricants. For evaluation, the coating is plasma spray deposited onto test journals which are slid against a superalloy partial arc foil bearing. The test load was 10 KPa (1.5 psi) and the bearings were run under start/stop cyclic conditions. The data show good wear performance of the bearing especially at temperatures above 25 °C. Bearing friction was moderate (μ ≤≈0.4) over the entire temperature range. Based upon the results obtained, the PS304 coating has promise for high temperature, oil-free turbomachinery applications.

Presented at the 54th Annual Meeting Las Vegas, Nevada May 23–27, 1999

KEY WORDS:

• Gas Bearings
• Solid Lubricants
• High Temperature

Notes

Presented at the 54th Annual Meeting Las Vegas, Nevada May 23–27, 1999