Effects of Loading and Sliding Speed on the Dry Sliding Wear Behavior of Mg-3Al-0.4Si Magnesium Alloy

, , , , , & show all
Pages 238-248 | Received 30 May 2015, Accepted 15 Feb 2016, Published online: 02 Aug 2016
 

ABSTRACT

The friction and wear properties of Mg-3Al-0.4Si alloy were investigated using a pin-on-disc tester. Morphologies and compositions of worn surfaces were characterized by scanning electron microscopy (SEM) and energy dispersive X-ray spectrometry (EDS) for identification of the wear mechanisms. Microstructural evolution and hardness change in subsurfaces were analyzed by confocal scanning laser microscopy and hardness testing. The results revealed that the wear behavior of Mg-3Al-0.4Si alloy was classified into two types of wear regimes; that is, mild and severe. In the mild wear regime, wear rates increased at a low slope with increasing load; the corresponding wear mechanisms were oxidation, abrasion, and delamination. In the severe wear regime, wear rates increased rapidly at a high slope with load; the wear mechanisms were severe plastic deformation and surface melting. Analysis of microstructural evolution on the subsurface identified the reason for the transition from mild to severe wear; that is, the realization of dynamic recrystallization (DRX) in the surface layer material. A contact surface DRX temperature criterion for the mild to severe wear transition was proposed, and the critical DRX temperatures for the mild to severe wear transition were calculated using DRX kinetics.

Funding

The authors express their gratitude for the support under the Project 985-Automotive Engineering of Jilin University, National Foundation of Doctoral Station (Grant No. 20110061110031) and National Natural Science Foundation of China (Grant No. 51201158).

Reprints and Corporate Permissions

Please note: Selecting permissions does not provide access to the full text of the article, please see our help page How do I view content?

To request a reprint or corporate permissions for this article, please click on the relevant link below:

Academic Permissions

Please note: Selecting permissions does not provide access to the full text of the article, please see our help page How do I view content?

Obtain permissions instantly via Rightslink by clicking on the button below:

If you are unable to obtain permissions via Rightslink, please complete and submit this Permissions form. For more information, please visit our Permissions help page.