Pore Structure Effects on Ca-Based Sorbent Sulfation Capacity at Medium Temperatures: Activated Carbon as Sorbent/Catalyst Support

Abstract

The reaction between three different Ca-based sorbents and SO₂ were studied in a medium temperature range (473–773 K). The largest SO₂ capture was found with Ca(OH)₂ at 773 K, 126.31 mg SO₂•g Ca(OH)₂ ⁻¹, and the influence of SO₂ concentration on the sorbent utilization was observed. Investigations of the internal porous structure of Ca-based sorbents showed that the initial reaction rate was controlled by the surface area, and once the sul-fated products were produced, pore structure dominated. To increase the surface area of Ca-based sorbents available to interact with and retain SO₂, one kind of CaO/activated carbon (AC) sorbent/catalyst was prepared to study the effect of AC on the dispersion of Ca-based materials. The results indicated that the Ca-based material dispersed on high-surface-area AC had more capacities for SO₂ than unsupported Ca-based sorbents. The initial reaction rates of the reaction between SO₂ and Ca-based sorbents and the prepared CaO/AC sorbents/cata-lysts were measured. Results showed that the reaction rate apparently increased with the presence of AC. It was concluded that CaO/AC was the active material in the des-ulfurization reaction. AC acting as the support can play a role to supply O₂ to increase the affinity to SO₂. Moreover, when AC is acting as a support, the surface oxygen functional group formed on the surface of AC can serve as a new site for SO₂ adsorption.