Abstract
Poor dispersion of nanoparticles in polymer matrix would limit the development and application of particulate-filled polymer composites. Therefore, the Sb2O3 nanoparticles were functionalized by a combination of cetyltrimethyl ammonium bromide (CTAB) and silane coupling agent KH-560 via water bath modification method so as to improve the dispersion of Sb2O3 nanoparticles in poly(butylene terephthalate) (PBT) matrix and enhance the interfacial adhesion between nanoparticles and polymer matrix. Besides, the coating efficiency of compound modifiers on the surface of Sb2O3 nanoparticles was characterized by Fourier transform infrared spectroscopy (FT-IR), thermogravimetric analysis (TGA). The Sb2O3 nanoparticles with different morphologies were systemically measured using transmission electron microscopy and dynamic light scattering measurement. The effects of particle surface treatment, particle size, particle morphology and particle loading on mechanical properties of composites were studied by the X-ray diffraction (XRD), tensile test machine and impact strength machine. The tensile strength of nanocomposites gradually increases with decreasing the particle size at the same amount of Sb2O3 nanoparticle fillers, which is attributed to improvement of interfacial contact area and stronger interfacial adhesion between Sb2O3 nanoparticles and PBT matrix. And the compound modified Sb2O3 nanoparticles are homogeneously dispersed in PBT matrix and play an important role in the properties enhancement. Moreover, taking consideration of the tensile and impact strengths, the optimal loading is 3 wt%.