Recent progress in sputtering PZT thin films for ferroelectric memories

Abstract

This paper describes amorphous Pb(Zr, Ti)O₃ (PZT) thin films deposited by cosputtering Pb(Zr_0.5 Ti_0.5)O₃ and PbO targets. By optimizing the amount of the excess Pb and the deposition temperature, PZT thin films with a single perovskite phase were obtained successfully on Ir substrates and Pt substrates at 520°C. 250-nm-thick PZT films crystallized by rapid thermal annealing (RTA) at 600°C for 20 s exhibited excellent ferroelectric properties: a coercive voltage of 1.0 V, a remanent polarization density of about 40 μC/cm², and a polarization switching endurance over 1x109 cycles. Although a heat treatment in a reductive ambient causes degradation of ferroelectric properties of PZT thin films, their degraded ferroelectric properties can be easily recovered from by a 1-min RTA in an oxygen at 400°C.

Key Words:

• amorphous PZT
• sputtering
• excess Pb
• hydrogen-damaged capacitor
• rapid thermal process
• ferroelectric memory