Preparation of Silica/Poly(tert‐butylmethacrylate) Core/Shell Nanocomposite Latex Particles

Nanocomposite latex particles, with a silica nanoparticle as core and crosslinked poly(tert‐butylmethacrylate) as shell, were prepared in this work. Silica nanoparticles were first synthesized by a sol‐gel process, and then modified by 3‐(trimethoxysilyl)propyl methacrylate (MPS) to graft C˭C groups on their surfaces. The MPS‐modified silica nanoparticles were characterized by elemental analysis, FTIR, and ²⁹Si NMR and ¹³C‐NMR spectroscopy; the results showed that the C˭C groups were successfully grafted on the surface of the silica nanoparticles and the grafted substance was mostly the oligomer formed by the hydrolysis and condensation reaction of MPS. Silica/poly(tert‐butylmethacrylate) core/shell nanocomposite latex particles were prepared via seed emulsion polymerization using the MPS‐modified silica nanoparticle as seed, tert‐butylmethacrylate as monomer and ethyleneglycol dimethacrylate as crosslinker. Their core/shell nanocomposite structure and chemical composition were characterized by means of TEM and FTIR, respectively, and the results indicated that silica/poly(tert‐butylmethacrylate) core/shell nanocomposite latex particles were obtained.

Keywords:

• inorganic/organic nanocomposite particles
• core/shell structure
• silica
• crosslinked poly(tert‐butylmethacrylate)
• 3‐(trimethoxysilyl)propyl methacrylate
• seed emulsion polymerization

Acknowledgements

This work was supported by the major project of science and technology research of the Educational Ministry of China (No.105077).