Synthesis and characterization of novel bisphthalonitrile resins linked by different molecular weight main-chain polybenzoxazines

ABSTRACT

A series of novel type bisphthalonitriles with different molecular weight main-chain polybenzoxazines as linkages have been successfully synthesized using 4, 4′-diaminodiphenyl methane, paraformaldehyde, bisphenol A and 4-nitrophthalonitrile as initial materials. The structures were characterized by Fourier transform infrared (FT-IR) and proton nuclear magnetic resonance (¹H-NMR). The formation of benzoxazine and the existence of nitrile groups were confirmed by the absorbance at 950cm⁻¹ of benzene attached with oxazine ring and 2231 cm⁻¹ of nitrile groups. The characteristic resonance peaks observed at about 4.52 (C-CH₂-N) and 5.28 ppm (N-CH₂-O) also determined the structure of benzoxazine ring. The curing behaviors were monitored by differential scanning calorimetry (DSC) and FT-IR. Two-stage polymerization mechanisms were observed according to the ring-opening of benzoxazine and the polymerization of nitrile groups catalyzed by phenolic hydroxyl groups, which generated during the curing reaction of benzoxazine. The polymerization of these bisphthalonitriles exhibited self-promoted curing behaviors. The completion of polymerization was proved by the disappearance of the band located at 950 cm⁻¹ in FT-IR. Thermogravimetric analysis (TGA) was used to investigate the thermal stability, and the results showed that the cured polymers achieved extremely high char yield from 61.1% up to 74.2% at 800°C under nitrogen and exhibited increasing decomposition temperature as the contents of phthalonitrile groups increased, which indicated that the polymerization of phthalonitriles could improve the thermal stability.

KEYWORDS:

• Phthalonitrile
• polybenzoxazine
• main-chain
• high-performance
• thermosetting resins

Funding

The authors gratefully acknowledge the financial support of the Key Laboratory of Cellulose and Lignocellulosics Chemistry.