Influence de la fumée de silice sur la résistance en compression des bétons à hautes performances

ABSTRACT

The admixture of silica fume reveals an increase in the compressive strength compared with a reference concrete during the first month. However the improvement of the compressive strength tends to disappear in the long run. Silica fume plays a positive part up to around 20% content and has the most important effect when reaching 10 to 15% content, regardless of the water-cementitious materials ratio (cement and silica fume).

The paper presents a prediction model of the compressive strength for silica fume concretes with or without air-entraining agents. That model is validated with a precision less than 5% thanks to 282 experimental data based on the authors 'experiments and other investigations.

RÉSUMÉ

L'ajout de fumée de silice en remplacement partiel du ciment se traduit par un accroissement de la résistance en compression par rapport à un béton de référence pendant le premier mois d'hydratation. A plus long terme cependant, le gain de résistance tend à s'annuler. La fumée de silice joue un rôle bénéfique jusqu'à des teneurs de 20% environ avec un effet optimum pour des pourcentages de l'ordre de 10 à 15% quel que soit le rapport eau sur liant (ciment plus fumée de silice). Un modèle de prévision de la resistance en compression de bétons avec fumée de silice est presenté. Ce modèle est validé avec une précision « meilleure que 5% » sur 282 données experimentales concernant des bétons avec ou sans entraineurs d'air dont les valeurs sont extraites de la littérature ou du travail des auteurs.

KEYWORDS:

• Portland Cement
• Silica Fume
• Superplasticizer
• Compressive Strength
• Model
• High-Strength Concrete
• Tricalcium Aluminate
• Hydration

MOTS-CLÉS:

• Ciment Portland
• Fumée de Silice
• Superplastifiant
• Résistance à la Compression
• Modèle, Béton à Haute Performance
• Aluminate Tricalcique
• Hydratation