La microfissuration superficielle a-t-elle une influence sur la profondeur de carbonatation des bétons?

ABSTRACT

This work deals with the influence of the superficial microcracking on concrete carbonation. Three types of concrete with strengths ranging between 25 and 60 MPa were subjected to different thermo-hygrometric treatments to create a superficial microcracking, then, to accelerated carbonation tests for 3 months. After their period of preconditioning treatments, the quantification of the superficial microcracking and the measure of the water absorption of the concrete were carried out to observe correlations with carbonation depth. Results show that the influence of the superficial microcracking is strongly dependant of the concrete strength and begins to be significant when concrete strength reaches about 50 MPa.

RÉSUMÉ

L'objectif de ce travail est d'analyser l'influence de la microfissuration de surface sur la carbonatation des bétons. Trois bétons dont les résistances varient de 25 à 60 MPa environ ont été fabriqués, soumis à différents traitements dessiccateurs afin de créer une microfissuration de surface, puis exposés pendant trois mois à une atmosphère enrichie en CO₂. A la fin de leur période de préconditionnement et avant leur exposition à l'ambiance enrichie en CO₂, la quantification de la microfissuration superficielle ainsi que la mesure du coefficient d'absorption d'eau des bétons ont été réalisées. Globalement, les résultats montrent que l'influence de la microfissuration superficielle sur la profondeur de carbonatation est très dépendante de la classe du béton considéré et commence à être significative pour des bétons atteignant des résistances de 50 MPa environ.

KEYWORDS:

• Concrete
• superficial microcracking
• water absorption
• carbonation

MOTS-CLÉS:

• béton
• microfissuration de surface
• absorption d'eau
• carbonatation