Mechanical properties, thermal and chemical effect of polymer cotton bars reinforced with carbon / glass fiber

ABSTRACT

Many researchers are interested in using natural fibres to treat due to recent advancements in polymer characteristics. The mechanical properties of three types of bars are studied in this paper: Cotton Fibre-Reinforced Polymer bars, Cotton/Carbon Fibre-Reinforced Polymer bars, and Cotton/Glass Fibre-Reinforced Polymer bars. The goal of the paper was to create low-cost bars with comparable mechanical performance and corrosion resistance to steel reinforcement. The bars were made using two methods: fibres immersed in polymer and fibres coated with polymer by repeated tension and relaxation of fibres. The second method produced better results in terms of the tensile strength of Cot.CFRP, Cot.GFRP, and Cot.FRP bars, which were 688, 477, and 284 MPa, respectively, and the stress–strain curve revealed brittle behaviour for all bars and modulus of elasticity of 43, 31 and 22 GPa. When sand was put on the bar’s surface, the bars demonstrated a good connection with the concrete. It also showed good resistance to moisture, alkaline solutions and acids, as well as heat resistance at temperatures below 200°C.

KEYWORDS:

• Cot.Cfrp (Cotton/carbon Fiber-Reinforced polymer)
• Cot.Frp (cotton fiber-reinforced polymer)
• Cot.Gfrp (cotton/glass fiber-reinforced polymer
• cotton fibre
• mechanical properties
• natural fibre

Disclosure statement

No potential conflict of interest was reported by the author(s).

Correction Statement

This article has been republished with minor changes. These changes do not impact the academic content of the article.

Additional information

Funding

The work was supported by the Luleå Tekniska Universitet [1].