![Sample our Engineering & Technology journals, sign in here to start your access, latest two full volumes FREE to you for 14 days]({"type":"image" , "src" : "/sda/5933/TOC-Subject-Sample-2021-Engineering-Tech.jpg"})
Abstract
The view that the intercalation of a polymer in an unmodified smectite clay is driven by the entropic increase that results from displacement of adsorbed water is re-assessed in the light of experiments that show rapid melt intercalation into a clay that has been heat-treated to remove gallery water. Dehydrated smectite clays with collapsed layers take up poly(ethylene glycol) from the melt in only 1 ks or from aqueous solution in under 18 ks, re-establishing the basal plane spacing to that for intercalation in untreated clay, 1.8 nm. Differential scanning calorimetry showed that the intercalation of poly(ethylene glycol) into montmorillonite is exothermic with an enthalpy change of −153 J g−1 based on the intercalated polymer and the heat of wetting for the internal surfaces of montmorillonite by poly(ethylene glycol) is −0.08 J m−2. These results confirm the observation of re-expansion of heat-treated clays and imply that the reduction in free energy on intercalation results from a significant enthalpic change as well as an entropic change for clays with interlayer water, and primarily from an enthalpic change for clay in the absence of water.
Acknowledgement
The authors are grateful to the Engineering and Physical Sciences Research Council for financial support under grant GR/R30907 which forms part of a collaboration with P.V. Coveney (University College London) and A. Whiting (University of Durham).