Critical conditions for dislocation nucleation at surface steps

Abstract

Dislocation nucleation at a surface step is analyzed based on a general variational boundary integral formulation of the Peierls–Nabarro dislocation model. By modelling the surface step as part of the surface of a three-dimensional crack, the free surface effect is taken into account by transferring the half space problem into an equivalent one in the infinite medium. The profiles of embryonic dislocations, corresponding to the relative displacements between the two adjacent atomic layers along the slip planes, are then rigorously solved through the variational boundary integral method. The critical conditions for dislocation nucleation are determined by solving the stress-dependent activation energies required to activate the embryonic dislocations from their stable to unstable saddle-point configurations. In particular, the effect of the step geometry, such as the height of the step, the dip angle of the slip plane and the inclined angle of the step surface on dislocation nucleation, is quantitatively ascertained. The results show that the atomic-scale surface step can rapidly reduce the critical stress required for dislocation nucleation from the surface by nearly an order of magnitude. The decrease in critical stress as a function of the height of the step is more significant for slip planes with smaller dip angles and surface steps with smaller inclined angles.

Acknowledgement

We gratefully acknowledge the support of the Lawrence Livermore National Laboratory and the National Science Foundation through the CAREER (0103257) and NIRT (0134446) awards.