SANS response of VVER440-type weld material after neutron irradiation, post-irradiation annealing and reirradiation

, , , , &
Pages 1855-1870 | Received 10 Mar 2006, Accepted 01 Nov 2006, Published online: 12 Mar 2007
 

Abstract

It is well accepted that the reirradiation behaviour of reactor pressure vessel (RPV) steel after annealing can be different from the original irradiation behaviour. We present the first small-angle neutron scattering (SANS) study of neutron irradiated, annealed and reirradiated VVER440-type RPV weld material. The SANS results are analyzed both in terms of the size distribution of irradiation-induced defect/solute atom clusters and in terms of the ratio of total and nuclear scattering intensity in a saturation magnetic field (A ratio). The measured A ratio is compared with calculations performed on the basis of the cluster composition reported for a similar weld material investigated by means of three-dimensional atom probe field ion microscopy. The observed deviation between both estimates and possible reasons for the discrepancy are discussed. Special emphasis is placed on the differences between the materials response to the original irradiation and to reirradiation after annealing. The results indicate that reirradiation-induced clusters are slightly different in their average composition and their formation saturates at a lower volume fraction than in the case of the original irradiation.

Reprints and Corporate Permissions

Please note: Selecting permissions does not provide access to the full text of the article, please see our help page How do I view content?

To request a reprint or corporate permissions for this article, please click on the relevant link below:

Academic Permissions

Please note: Selecting permissions does not provide access to the full text of the article, please see our help page How do I view content?

Obtain permissions instantly via Rightslink by clicking on the button below:

If you are unable to obtain permissions via Rightslink, please complete and submit this Permissions form. For more information, please visit our Permissions help page.