Nucleation of dynamic recrystallization and variant selection in copper bicrystals

, , &
Pages 4197-4209 | Received 11 Apr 2007, Accepted 20 Jun 2007, Published online: 17 Aug 2007
 

Abstract

Orientation-controlled copper bicrystals containing [001] symmetrical tilt boundaries aligned parallel to the loading axis were deformed in tension at 923 K and a strain rate of 4.2 × 10−4 s−1. The nucleation of dynamic recrystallization (DRX) was investigated along the grain boundary. For this purpose, both optical and orientation imaging microscopy methods were used. After grain-boundary migration (GBM) and bulging, nuclei appeared behind the most deeply indented grain boundary regions. The critical strain for nucleation was about one-quarter to one-half of the peak strain and depended on the misorientation angle. All the nuclei were twin-related (Σ3) to the matrices. Furthermore, all the primary twin traces were parallel to those of the inactive slip planes of the parent single crystals. Crystallographic analysis revealed the important role of the direction of GBM on twinning-plane variant selection. The characteristics of grain boundary nucleation depended sensitively on grain boundary character and on grain boundary mobility. The observed DRX nucleation mechanism is discussed in relation to the occurrence of GBM and twinning.

Reprints and Corporate Permissions

Please note: Selecting permissions does not provide access to the full text of the article, please see our help page How do I view content?

To request a reprint or corporate permissions for this article, please click on the relevant link below:

Academic Permissions

Please note: Selecting permissions does not provide access to the full text of the article, please see our help page How do I view content?

Obtain permissions instantly via Rightslink by clicking on the button below:

If you are unable to obtain permissions via Rightslink, please complete and submit this Permissions form. For more information, please visit our Permissions help page.